Nowadays several technologies rely on sintering to transform porous, fragile
parts into sturdy, fully dense components: from powder pressing
to metal injection moulding, moving to binder jetting additive
manufacturing and metal FDM (Fused Deposition Modelling).
Stainless-steel components represent a large part of the market for sintered
parts; they can be produced using any of the technologies mentioned above and have
a wide variety of applications such as automotive, biomedical
industries, mechanical and fashion.
Among the most widespread stainless steels used for sintering are the 304L, 316L,
440, 410 and 17-4 PH, which are chosen for their mechanical properties together
with their exceptional corrosion resistance.
In this article we are going to discuss how sintering parameters, and especially
the sintering atmosphere, may affect the quality achievable from sintered stainless-steel
We’ll analyse the three gas options, and we’ll see that in some circumstances
there are interesting solutions that can fit your needs. Read on!
Introduction to Vacuum Sintering
The atmosphere plays an essential role in the successful outcome of the sintering
process, for this reason the sintering atmosphere must be carefully selected in
relation to the material and the final application.
Sintering under vacuum (which is in fact a reducing atmosphere)
has several advantages:
- Bright parts after sintering.
- Lack of oxidation and/or atmosphere contamination.
- Precise setting and monitoring of the process parameters.
Some material must be sintered under vacuum with pressure ranging between 10-2
millibars and 10-4 millibars. Those are, for example, the best
condition for sintering extremely reactive materials, such as titanium.
However, most of the sintered materials requires atmospheres enriched with inert
gases, which is also the case for stainless steels.
The starting condition is always a cold furnace that has reached the proper vacuum
level, which is then backfilled (partial pressure or over-pressure) with inert gas.
This leads to the following benefits:
- The depletion of alloying elements can be avoided (i.e. chromium and manganese).
- The elimination of residual binder is eased by a continuous flow of gas,
which is constantly pumped out of the furnace chamber.
- The oxygen content on the parts can be controlled by exploiting the reducing
capacities of the process gases used and/or of the vacuum itself.
- The carbon content of the processed parts can be controlled.
Process gas for vacuum sintering of stainless steel
The gases used as a protective atmosphere inside a vacuum furnace are most commonly:
Nitrogen: it is an inert gas and the less expensive among
the process gas, for this reason it is widely used for sintering applications.
Argon: it is more expensive than the nitrogen therefore
it is chosen as an inert gas mostly when the processed material is nitrogen
Hydrogen: it is the most expensive among the listed gases
and has safeties implications for both the furnace and the installation site
of the furnace itself. However, hydrogen is an extremely reducing agent.
If we focus on the sintering of stainless steels, all the of the above-mentioned
atmospheres are viable choices.
Let's briefly delve into the topic, highlighting the pros and cons of the 3 process
Did you like this article up to here?
Before you continue, follow us on our LinkedIn page pressing the button here below!
In this way, we'll be able to keep you updated on most advanced technologies for heat treatments not only with our posts, but also with the best articles that we collect around the web.
Nitrogen is soluble in the steel matrix and act as a solid solution strengthening
in austenitic stainless steels.
Nitrogen can form nitrides at high temperature.
Focusing on stainless steel, chromium nitrides precipitation can affect the corrosion
resistance of the part by forming sensitized regions that act as corrosion initiator.
For this reason, high cooling rates are often adopted after sintering
in nitrogen to minimize the phenomena.
For some stainless steels, nitriding during the sintering process is a requirement
to obtain the desired properties and microstructure. This is, for example, the case
of the nickel free stainless steel X15CrMnMoN17-11-3 (Catamold ® PANACEA) that
is usually sintered using a high partial pressure of nitrogen of around 700 mbar.
Usually, pure Argon is not an optimal for processing stainless steel.
In fact, Argon is not soluble in the steel matrix, and may generate porosity due
to the gas trapped inside the part.
Hydrogen is widely used for the sintering of stainless steel
due to its ability of reducing oxides, thus helping to obtain clean parts.
Hydrogen also plays an important role in the carbon control of the parts by removing
the residual carbon left by the binder itself at the end of the binder burnout (since
binders typically used in powder metallurgy are carbon based).
Hydrogen can be used in vacuum furnaces with both partial pressure (0,1 –
10 mbar) and with slightly over-pressure (backfilling with approx. 1.1 bar hydrogen).
However vacuum furnaces operating with hydrogen require additional safety
For this reason, specific design solutions (such as double seals on all the furnace
flanges) and software safeties are adopted.
Despite the increased degree of complexity of the equipment and the higher process
costs, vacuum furnaces operating with hydrogen over-pressure bring several advantages:
- Oxygen cannot enter in the furnace under any circumstance since the furnace
- There are more reactive hydrogen molecules available in the furnace compared
to partial pressure atmosphere, therefore maximizing the reductive power.
Hydrogen mixtures, a valuable alternative
Under some circumstances, the use of inert gas (nitrogen or argon) and hydrogen
mixtures can be a good trade-off.
In fact, they retain some of the reducing capability specific of pure hydrogen atmosphere
while lowering the operating and investment costs.
Moreover, mixtures of inert gases with low hydrogen percentage (>5.5 mol% hydrogen
in nitrogen and >3 mol% hydrogen in argon) can be used without implementing
the safety measures that are required with hydrogen over-pressure.
Argon-based mixtures are typically preferred to avoid chromium nitrides
precipitation during cooling when high cooling rates cannot be achieved,
while Nitrogen ones are used for all the other cases.
All the gas alternatives discussed in this article are viable choices for the
sintering of the stainless-steel parts, however a thorough analysis is crucial to
achieve the desired properties.
Choosing the right sintering atmosphere for your process may help you get the
best trade-off between results and operating costs.
Do you have a question on this topic?
Freely write it in the comments section of this article or, if you want more information
on vacuum sintering, download the free eBook here below.
Download the FREE eBook
Download the FREE guide to vacuum sintering and get deep insight into the heat treatment process to improve your products.
Learn how powdered metal, metal injection molding (MIM), 3D printing and other similar technologies can benefit greatly from the superior quality and flexibility of vacuum sintering.